Conditions Extrêmes et Matériaux : Haute Température et Irradiation
CEMHTI - UPR3079 CNRS
utilisateur non identifié |
Login
Home
Directory
Publications
Research
Facilities
Jobs - News
Access
Past members
CERAM - M.Allix
DEFIR - P.Desgardin
MatRMag - V.Montouillout
NAFMAT - C.Ania
OR2T - O.Rozenbaum
Common Actions
High-Temperatures Facility
Particles Beams Facilities
Vibr. Spectroscopies and Planex
NMR Facility
Softwares
National and European Facilities
all the instruments
Pelletron
Positons
Performances
IBA Techniques
Implantation and Irradiation
IR-RMN in Infranalytics
PANACEA Eu
850 MHz
Diffusion
NMR
dmfit NMR
focus (IR Optics)
Levitation
Electron Microscope
XRay and Neutrons
NMR
IR emission
RAMAN
Accelerators
RAMAN in situ
RAMAN high temp.
RAMAN imaging
News@CEMHTI
Jobs@CEMHTI
Seminars@CEMHTI
View CEMHTI Publication
Return to publication search...
Ask for a reprint
email :
I am not a bot ;-)
2019
ACL
doi
A.B.Kuriganova, N.A.Faddeev, I.N.Leontyev, M.Allix, A.Rakhmatullin, N.V.Smirnova
,
'New Electrochemical Approach for the Synthesis of Pd‐PdO/C Electrocatalyst and Application to Formic Acid Electrooxidation'
, ChemistrySelect 4 8390–8393 (2019) doi:
10.1002/slct.201901628
Pd‐PdO/C catalyst for formic acid electrooxidation has been synthesized via electrochemical dispersion of Pd foil electrodes under pulse alternating current conditions in NaCl aqueous electrolyte. About 35 wt% of the as‐prepared Pd‐PdO/C specimen is PdO as revealed by X‐ray diffraction. The microstructural characteristics and catalytic activity of the synthesized Pd/C catalyst have been compared with those of a Pt/C catalyst prepared under the same conditions. Pd nanoparticles of Pd‐PdO/C catalyst exhibit smaller average dimensions and narrower particle size distribution – 7.4±0.5 nm and 1.9±0.5 respectively for Pd and PdO particles. The process of ethanol electrooxidation on the catalyst was characterized by high overvoltage (up to 800 mV). The overvoltage of the formic acid electrochemical oxidation on Pd/C is 590 mV less than on Pt/C.